AVUE AvueT Crown - Flurorescent Tempory & Bridge Material

AVUE AvueT Crown - Fluorescent Temporary Crown & Bridge Material<10:1>.

AvueT Crown is a self-curing composite for natural looking long and short term temporization. It is automatically mixed and available in the mixing ratio of 10:1.AvueT Crown is dispensed from preloaded syringes or cartridges and mixed through an automix tip. This provides consistent mixtures with no air incorporation into the final mix. 

AvueT Crown have very low exothermic setting reactions, unlike the methacrylates, and are less irritant to the underlying pulpal tissue. Additionally, they have low shrinkage, providing good marginal fit with good transverse strength and abrasion resistance. 

AvueT Crown better indicated for anterior temporaries because of their improved esthetics. 

Physical properties: temperature increase

• The temperature increase during the setting reaction of AVUE T CROWN is measured according to ISO 4049: The material is mixed at room temperature and the curing process is initiated at a starting temperature of 37°C.
• AVUE T CROWN shows a low temperature increase during the setting reaction and thus, it is very comfortable for the patient and without pulp irritations.

Mechanical properties: flexural strength

• The flexural strength is determined from the 3-Point bending experiment.
  Mechanical stability is important for the clinical success of provisional crown &
  bridge materials. Flexural strength of AvueT crown is superior than its competitors making it  a very good prediction of the clinical
• performance in the mouth.
  

Mechanical properties: compressive strength

The measurement of compressive strength is a good prediction of clinical performance of small temporaries (crowns, inlays). Like with all in-vitro tests it represents only a part aspect of the real clinical situation. Therefore the summary
of all mechanical testing experiments have to be viewed as a prediction of the
clinical situation.

Mechanical properties: Summary

AVUE T CROWN has well balanced mechanical properties, which are comparable or better than the leading competitors in the market. This assures a very good clinical performance.

Benefits:

1. High fracture resistance.
2. Ultimate compressive strength of 320 mpa.
3. Low temperature increase during setting.
4. Easy to trim & polish.
5. Methylmethacrylate free.
6. Amazing aesthetic with natural fluorescence.
7. Easy automix application
8. Excellent polishability.
9. Low shrinkage enables precision fit.